www.finnedtubes.cn | Site map | Contact | Download Catalogue | Print | Favorite | 中文magvant.cn
IK-CHINA LIMITED
news
Home
Boiler tubes

Heat exchanger tubes

Welded pipes

L, LL, KLM finned tubes (fin tubes)

high frequency welded (serrated) finned tubes (fin tubes)

(serrated) extruded finned tubes

hot dipped galvanized oval (elliptical) finned tubes, rectangular fin tubes

condenser fin flat tubes

H / double H finned tubes (fin tubes)

Studded Pipes

Laser welded finned tubes (fin tubes)

G embedded finned tubes (fin tubes)

inner finned tubes (fin tubes)

longitudinal finned tubes (fin tubes)

seamless finned tubes with two longitudinal opposite fins

casting alloy tubes

Tube finning machine

Aluminum plates, strips,foils

Aluminum welding wire rod

Aluminum tubes, profile

Economizer for Boiler

air-cooled heat exchanger (air cooler)

material

standard & specification

 
Chrome Moly AISI 4130
Chrome Moly AISI 4130
Chemistry Data,
Composition,%:
Carbon 0.28 0.33
Chromium 0.8 1.1
Manganese 0.7 0.9
Molybdenum 0.15 0.25
Phosphorus 0.035 max
Silicon 0.15 0.35
Sulphur 0.04 max

Design Features
AISI 4130 is a low alloy steel containing molybdenum and chromium as strengthening agents. The carbon content is nominally 0.30% and with this relatively low carbon content the alloy is excellent from the fusion weldability standpoint. The alloy can be hardened by heat treatment.

Typical applications for 4130 low alloy steel include. structural use such as aircraft engine mounts and welded tubing applications.

Machinability
This alloy is readily machined by conventional methods. Machinability is best with the alloy in the normalized and tempered condition. Although the alloy may be machined in the fully heat treated condition, machinability becomes more difficult with increasing strength (hardness) of the alloy.
Formability is best in the annealed condition for which the ductility is very good, Bend radii of 1t on annealed sheet material may be made.

Heat Treatment
Heating at 1600 F followed by an oil quench will harden the 4130 alloy. For best results a normalizing prehardening heat treatment may be used at 1650 to 1700 F followed by the 1600 F soak and oil quench.

Forging
Forge at 2200 F maximum down to 1750 F.

Hot Working
4130 in the annealed condition has excellent ductility. Thus it is usually not necessary to do hot working to form parts. If hot working is needed it can be done in the range of 2000 F to 1500 F.

Cold working by conventional methods is readily accomplished on this alloy.

Annealing
4130 (and most of the other low alloy steels) may be annealed at 1550 F for a time long enough to allow thorough heating of the section size. It should then be cooled in the furnace at a rate of less than 50 F per hour down to 900 F, followed by air cooling from 900 F.

Tempering
Tempering is done to restore some of the ductility that may be lost after the hardening heat treatment and quench. Alloy 4130 is tempered at between 750 F and 1050 F, depending upon the strength level desired. The lower the tempering temperature the greater the strength.


Hardening is accomplished by heat treatment or by cold working see "Heat Treatment".


Physical Data :
Density (lb / cu. in.) 0.283
Specific Gravity 7.8
Specific Heat (Btu/lb/Deg F [32212 Deg F]) 0.114
Melting Point (Deg F) 2610
Thermal Conductivity 22.3
Mean Coeff Thermal Expansion 7
Modulus of Elasticity Tension 29
 